b'GC195 KEY TECHNICAL FEATURES: -Gel Time (ICON 002) (20C2% MEKP on 100gr)10-14 min ISO/NPG Gelcoat Brookfield Viscosity 5 rpm : 140 - 200 PoiseSanitaryware (ISO2555 - 20Csp6) 50 rpm : 22 - 28 PoiseFlexural strength 113 MPa Tensile strength 63 MPa Elongation at break 4% SPRAY Barcol Hardness45Topcoat version (TC195) With wax addition for tack free finishGC195 is a spray isophthalic Neopentyl Glycol based Polyester gelcoat developed for superior UV weathering performance in the most testing environments. Excellent colour and gloss retention over time, superb water resistance with very low pick-up, high resistance to osmosis blistering, tough, long-lasting and durable surface, excellent handling.GC794 KEY TECHNICAL FEATURES: -Gel Time (ICON 002)8 - 12 minutesISO/NPG Gelcoat (20C2% MEKP on 100gr) Brookfield Viscosity 5 rpm : 150 - 210 PoiseIdeal for Swimming (ISO2555 - 20Csp6) 50 rpm : 35 - 45 PoisePools and Ponds Flexural strength 107.9 MPa Elongation at break 2.85% Barcol Hardness 50Temperature of deflection72CBRUSH ROLLER under load* (HDT)Flexural modulus* (ISO 178)4.38 GPaGC794 is a brush isophthalic Neopentyl Glycol based Polyester gelcoat developed for Excellent colour and gloss retention over time, superb water resistance with very low pick-up, high resistance to osmosis blistering, tough, long lasting and durable surface, excellent handling. It is formulated for swimming pool industry. Pre-accelerated and thixotropic gel coat. Roller application. No drainage on vertical surfaces. High quality of covering power. Excellent water resistance and chlorine resistance.GC860 KEY TECHNICAL FEATURES: -Gel Time (ICON 002)22 - 28 min ISO/NPG Gelcoat (20C2% MEKP on 100gr) Brookfield Viscosity 5 rpm : 100 - 140 PoisesIdeal for(ISO2555 - 20Csp6) 50 rpm : 19 - 25 Poise Sanitary Ware Flexural strength 134.6 MPa Elongation at break 4.01 %Barcol Hardness 45-45 Temperature of deflection70CSPRAY under load* (HDT)Flexural modulus* (ISO 178)3.93GPa GC 860 is a spray isophthalic Neopentyl Glycol based Polyester resistance. It is recommended for a use in the sanitary industry. Thixotropic and pre-accelerated, formulated for spray application. Good resistance to thermal shock.'