b'Epoxy Bonding GelcoatsGC250 KEY TECHNICAL FEATURES: -Gel Time (ICON 002) (20C2% MEKP on 100gr)10 - 14 minEpoxy BondingBrookfield Viscosity (ISO2555 - 20Csp6) 5 rpm : 120 - 180 PoiseGelcoat based on50 rpm : 35 - 45 Poise Vinyl Ester Flexural strength143.7 MPa Tensile Strength44.93 MPa Barcol Hardness45 Temperature of deflection under load* (HDT) 105CElongation at break 2.66%BRUSH SPRAYA pre-accelerated and thixotropic gelcoat available in brush and spray variants (GC251). Pigmented to any RAL or BS shade. Low Styrene GC8100KEY TECHNICAL FEATURES: -Gel Time (ICON 002) (20C2% MEKP on 100gr)10 - 14 minLow styrene Brookfield Viscosity (ISO2555 - 20Csp6) 5 rpm : 140 - 200 Poise 50 content rpm : 22 - 28 Poise S.G 1,30 - 1.41 g/cm 3Pre-AcceleratedGC8100 is based on an Isophthalic polyester resin. It is recommended for the production of industrial parts. Thixotropic and pre-accelerated.Formulated for spray application. Cures at ambient temperature by addition of MEKP (type Butanox M50) catalyst. Low styrene content. Good abrasion resistance according to NF14688 SPRAY (Indicative test).'